Nickel based-superalloys are used in applications requiring strength at high temperatures. Most of these alloys are precipitation hardened by a γ'[(Al,Ti)] phase coherently precipitated in a fcc matrix. The properties and resistance to microestructural changes at high temperatures depend on factors such as particle size, coarsening rate, distribution and volume fraction of the γ precipitate, factors that can be modified through different heat treatments. The present work describes the effect of heat treatments to produce different γ'[(Al,Ti)] precipitate sizes and distribution in a CMSX-2 superalloy. Using subsequent aging treatment at constant temperature, we studied de evolution and growth of such precipitate particles and determined the activation energy for coarsening.

Las superaleaciones base níquel son utilizadas en aplicaciones tecnológicas que requieren gran resistencia a altas temperaturas. Muchas de estas aleaciones son endurecidas por precipitación de una fase coherente γ'[(Al,Ti)] precipitada en una matriz FCC. Las propiedades y resistencia a los cambios microestructurales dependen de factores como: velocidad de crecimiento, distribución, fracción de volumen y tamaño de partícula, factores estos que pueden ser controlados por medio de diferentes tratamientos térmicos. El presente trabajo describe el efecto de los tratamientos térmicos de solubilizado, post-solubilizado y precipitado para producir distintos tamaños y distribución de partículas γ'[(Al,Ti)] en una superaleación CMSX-2 y posteriormente se estudió a través de diferentes tratamientos térmicos de envejecimiento a temperatura constante, la evolución, crecimiento y energía de activación para el crecimiento de las partículas precipitadas.